Two Component Blend Polyol Rigid Foam For Building System
DESCRIPTION
SDA13E cold storage insulation system blend polyol is a kind of spray rigid PU foam blend polyol, specially used for the insulation of the wall of storage insulation. It used together with isocyanate(PM-200) to make rigid PU foam through PU spray machine. The foam produced has the characteristics as following:
Importance:The above mentioned are typical test values, and the specific data may vary slightly due to environmental conditions.For our products, the data are not legally binding.
COMPONENT PRODUCT SPECIFICATIONS
REACTIVITY PROFILE
INSTALLATION GUIDELINE
SD1133:PM200=1:1(volume ratio)
Foaming Machine:Polyurethane Rigid foam Spray Machine
ADDITIONAL INFORMATION
220KGS/Drum, Blue paint or Zinc coating drums (Drum Weight:18-23kg)
STORAGE RECOMMENDATIONS
The blend polyol should be stored in the sealed container to avoid the absorption of water vapor.During the transportation, it should avoid serious shake and strong sunlight.It should be stored in ventilated place, avoiding light, water and fire.Recommended storage temperature is 15~25ºC.
Shelf life:6 months, please test before using after 6 months storage.
DESCRIPTION
SDA13E cold storage insulation system blend polyol is a kind of spray rigid PU foam blend polyol, specially used for the insulation of the wall of storage insulation. It used together with isocyanate(PM-200) to make rigid PU foam through PU spray machine. The foam produced has the characteristics as following:
- The strong adhesive force, convenient construction and no seams.
- The low thermal conductivity, low water absorption and good dimensional stability.
- The long service life.
| Physical Properities | Test Method | Metric | Value | |
| Core Density | GB/T 6343-2009 | Kg/m3 | 45.3 | |
| Compressive Strength | GB/T 8813-2008 | KPa | 264 | |
| Tensile Strenght | GB/T 9641-88 | KPa | 136 | |
| Oxygen index | GB/T 2406.2-2009 | % | 23.4 | |
| Initial Thermal Conductivity | GB/T 10294-2008 | W/(m·K) | 0.022 | |
| Close Cell Content | GB/T 10799-2008 | % | ≥88 | |
| Water Absorption | GB/T 8810-2005 | % | ≤3 | |
| Dimensional Stability (Foam made After 6 days) | -25ºC | GB/T 8811-2008 | % | ≤±1 ≤±1 |
| 70ºC | ||||
COMPONENT PRODUCT SPECIFICATIONS
| Property | Blend polyol SDA13E | Polymeric MDI Pm200 |
| Appearance | Pale yellow liquid. | Brown liquid |
| Specific gravity at 25°C | 1.10±0.10 g/cm3 | 1.22-1.25 g/cm3 |
| Viscosity at 25°C | 300±100 cps | 200±50 cps |
| Shelf life | 3 months | 12 months |
| Cream Time | Gel Time | Rise Time |
| 0-1 s | 2-3 s | 4-6 s |
INSTALLATION GUIDELINE
| SD1133 | Ambient Temperatures | Spraying Temperatures | Minimum Spray Pressures |
| Summer | 10-35ºC | 35-41ºC | 5516kPa (800 psi) |
| Sping~Autumn | 0-15ºC | 35-45ºC | 5516kPa (800 psi) |
| Winter | -10-5ºC | 35-50ºC | 5516kPa (800 psi) |
Foaming Machine:Polyurethane Rigid foam Spray Machine
ADDITIONAL INFORMATION
- Maximum per pass thickness is 35mm,Spraying thicker can result in spontaneous combustion and poor overall spray foam quality
- Internal temperature of installed pass must be 25ºC before installing subsequent passes Maximum thickness during 24h period is 203mm(8inches)
- Like most of foam product,foam made by SD1133is combustible,An thermal barrier must be installed in accordance with approved construction standards SD1133
- The service temperature of the foam with SD1133 is between -60~80ºC.
220KGS/Drum, Blue paint or Zinc coating drums (Drum Weight:18-23kg)
STORAGE RECOMMENDATIONS
The blend polyol should be stored in the sealed container to avoid the absorption of water vapor.During the transportation, it should avoid serious shake and strong sunlight.It should be stored in ventilated place, avoiding light, water and fire.Recommended storage temperature is 15~25ºC.
Shelf life:6 months, please test before using after 6 months storage.